Electrochromism of sputtered fluorinated titanium oxide thin films

A. Gutarra; A. Azens; B. Stjerna; C. G. Granqvist

doi:10.1063/1.111851

Electrochromism of sputtered fluorinated titanium oxide thin films

A. Gutarra
, A. Azens
, B. Stjerna
, C. G. Granqvist

Producción científica: Contribución a una revista › Artículo (Contribución a Revista) › revisión exhaustiva

42 Citas (Scopus)

Resumen

Titanium-oxide-based films were prepared by reactive dc magnetron sputtering in Ar+O₂+CF₄. Pronounced electrochromism was found in LiClO₄+propylene carbonate. The maximum coloration efficiency was 37 cm²/C at a wavelength of ∼0.7 μm. Polaron hopping is believed to cause the absorption. Coloration/bleaching was performed for up to 2×10⁴ cycles without apparent degradation.

Idioma original	Inglés
Páginas (desde-hasta)	1604-1606
Número de páginas	3
Publicación	Applied Physics Letters
Volumen	64
N.º	13
DOI	https://doi.org/10.1063/1.111851
Estado	Publicada - 1 dic. 1994
Publicado de forma externa	Sí

Acceder al documento

10.1063/1.111851

Otros archivos y enlaces

https://www.scopus.com/pages/publications/0028386172

Citar esto

@article{64c3ce2f3ab4404eb69dd618dd4b01e5,

title = "Electrochromism of sputtered fluorinated titanium oxide thin films",

abstract = "Titanium-oxide-based films were prepared by reactive dc magnetron sputtering in Ar+O2+CF4. Pronounced electrochromism was found in LiClO4+propylene carbonate. The maximum coloration efficiency was 37 cm2/C at a wavelength of ∼0.7 μm. Polaron hopping is believed to cause the absorption. Coloration/bleaching was performed for up to 2×104 cycles without apparent degradation.",

author = "A. Gutarra and A. Azens and B. Stjerna and Granqvist, \{C. G.\}",

year = "1994",

month = dec,

day = "1",

doi = "10.1063/1.111851",

language = "Ingl{\'e}s",

volume = "64",

pages = "1604--1606",

journal = "Applied Physics Letters",

issn = "0003-6951",

publisher = "American Institute of Physics",

number = "13",

}

TY - JOUR

T1 - Electrochromism of sputtered fluorinated titanium oxide thin films

AU - Gutarra, A.

AU - Azens, A.

AU - Stjerna, B.

AU - Granqvist, C. G.

PY - 1994/12/1

Y1 - 1994/12/1

N2 - Titanium-oxide-based films were prepared by reactive dc magnetron sputtering in Ar+O2+CF4. Pronounced electrochromism was found in LiClO4+propylene carbonate. The maximum coloration efficiency was 37 cm2/C at a wavelength of ∼0.7 μm. Polaron hopping is believed to cause the absorption. Coloration/bleaching was performed for up to 2×104 cycles without apparent degradation.

AB - Titanium-oxide-based films were prepared by reactive dc magnetron sputtering in Ar+O2+CF4. Pronounced electrochromism was found in LiClO4+propylene carbonate. The maximum coloration efficiency was 37 cm2/C at a wavelength of ∼0.7 μm. Polaron hopping is believed to cause the absorption. Coloration/bleaching was performed for up to 2×104 cycles without apparent degradation.

UR - https://www.scopus.com/pages/publications/0028386172

U2 - 10.1063/1.111851

DO - 10.1063/1.111851

M3 - Artículo (Contribución a Revista)

AN - SCOPUS:0028386172

SN - 0003-6951

VL - 64

SP - 1604

EP - 1606

JO - Applied Physics Letters

JF - Applied Physics Letters

IS - 13

ER -

Electrochromism of sputtered fluorinated titanium oxide thin films

Resumen

Acceder al documento

Otros archivos y enlaces

Huella

Citar esto